| Properties | PP + 30% HF |
Young Modulus (GPa) | 1.8 |
Re (Mpa) 25 mm/min | 19 |
Rm (Mpa) 25 mm/min | 25 |
A (%) 25 mm/min | >260 |
MFI (g/10 min) 2.16 kg/230°C | 6.5 |
Hardness (Shore D) | 68 |
Density (kg/m3) | 980 |
Barrel Temperature (°C) | 180-230 |
Mould Temperature (°C) | 40-70 |
Drying Temperature (°C) | 60-80 (3h) |
Shrinkage (%) | 1.8 |
Resistivity (ohm cm) | >10.12 |
Vicat Softening Point (°C) | 100 |